Investment Casting

Investment Casting


                                

Investment casting is a manufacturing process in which a wax pattern is coated with a refractory ceramic material. Once the ceramic material is hardened its internal geometry takes the shape of the casting. The wax is melted out and molten metal is poured into the cavity where the wax pattern was. The metal solidifies within the ceramic mold and then the metal casting is broken out. This manufacturing technique is also known as the lost wax process. Investment casting was developed over 5500 years ago and can trace its roots back to both ancient Egypt and China. Parts manufactured in industry by this process include dental fixtures, gears, cams, ratchets, jewelry, turbine blades, machinery components and other parts of complex geometry.




The Process

The first step in investment casting is to manufacture the wax pattern for the process. The pattern for this process may also be made from plastic; however it is often made of wax since it will melt out easily and wax can be reused. Since the pattern is destroyed in the process, one will be needed for each casting to be made. When producing parts in any quantity, a mold from which to manufacture patterns will be desired. Similar to the mold that may be employed in the expanded polystyrene casting process to produce foam polystyrene patterns, the mold to create wax patterns may be cast or machined. The size of this master die must be carefully calculated. It must take into consideration shrinkage of wax, shrinkage of the ceramic material invested over the wax pattern and shrinkage of the metal casting. It may take some trial and error to get just the right size, therefore these molds can be expensive.

Figure:48 


mold for producing patterns 




Since the mold does not need to be opened, castings of very complex geometry can be manufactured. Several wax patterns may be combined for a single casting. Or as often the case, many wax patterns may be connected and poured together producing many castings in a single process. This is done by attaching the wax patterns to a wax bar, the bar serves as a central sprue. A ceramic pouring cup is attached to the end of the bar. This arrangement is called a tree, denoting the similarity of casting patterns on the central runner beam to branches on a tree.

Figure:49 


Wax Pattern Tree 




The metal casting pattern is then dipped in a refractory slurry whose composition includes extremely fine grained silica, water and binders. A ceramic layer is obtained over the surface of the pattern. The pattern is then repeatedly dipped into the slurry to increase the thickness of the ceramic coat. In some cases the pattern may be placed in a flask and the ceramic slurry poured over it.

Figure:50 


Refractory Slurry Invested Over Wax Pattern 




Once the refractory coat over the pattern is thick enough, it is allowed to dry in air in order to harden.

Figure:51 


Refractory Coat Drying In Air 




The next step in this manufacturing process is the key to investment casting. The hardened ceramic mold is turned upside down and heated to a temperature of around 200F-375F (90C-175C). This causes the wax to flow out of the mold, leaving the cavity for the metal casting.

Figure:52 


Wax Being Melted Out Of Investment Mold 




The ceramic mold is then heated to around 1000F-2000F (550C-1100C). This will further strengthen the mold, eliminate any leftover wax or contaminants and drive out water from the mold material. The metal casting is then poured while the mold is still hot. Pouring the casting while the mold is hot allows the liquid metal to flow easily through the mold cavity, filling detailed and thin sections. Pouring the metal casting in a hot mold also gives better dimensional accuracy, since the mold and casting will shrink together as they cool.

Figure:53 


Mold For Investment Casting Heated Before Pouring 




Figure:54 


Pouring Of An Investment Casting 




After pouring of the molten metal into the mold, the casting is allowed to set as the solidification process takes place.

Figure:55 


Solidification Of An Investment Casting 




The final step in this manufacturing process involves breaking the ceramic mold from the investment casting and cutting the parts from the tree.

Figure:56 


Break Up Of The Mold For An Investment Casting 




Figure:57 


Final Product Of Investment Casting 






Properties And Considerations Of Manufacturing By Investment Casting

  • Investment casting is a manufacturing process that allows the casting of extremely complex parts, with good surface finish. 


  • Very thin sections can be produced by this process. Metal castings with sections as narrow as .015in (.4mm) have been manufactured using investment casting. 


  • Investment casting also allows for high dimensional accuracy. Tolerances as low as .003in (.076mm) have been claimed. 


  • Practically any metal can be investment cast. Parts manufactured by this process are generally small, but parts weighing up to 75lbs have been found suitable for this technique. 


  • Parts of the investment process may be automated. 


  • Investment casting is a complicated process and is relatively expensive. 